Braskem PE TX7001
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P8uAT5_Braskem-PE-TX7001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TX7001 is a low-density polyethylene (LDPE) with high molecular weight, designed to satisfy those applications that require high mechanical strength and environmental stress cracking resistance (ESCR), together with good processability, proper of branched polyethylene produced by a high-pressure process. TX7001 resin presents an excellent performance in conventional LDPE extruders, granting low energy consumption during the whole process and allowing the production of packaging with a good dimensional uniformity and an excellent surface finishing. This product is identified as PE 115 according to ASTM D-4976-04a standard specification. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.922 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.14 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 150 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 170 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 360 | % | |
| TD : Break, 50 µm, Blown Film | 740 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 200 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, Blown Film | 180 | g | |
| TD : 50 µm, Blown Film | 200 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 45°, 50.0 µm, Blown Film | 33 | ||
| 60°, 50.0 µm, Blown Film | 53 | ||
| Haze (50.0 µm, Blown Film) | 19 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 to 225 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 G3 X0 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Trexlink™ 4770 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | Trexlink™ |
| Aurora PVC AP1250 Series | Aurora Plastics, Inc. | PVC, Unspecified | Aurora PVC |
| DeWAL DW 402B | DeWAL Industries | UHMWPE | DeWAL |
| Polifor® 6 GF/30 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |