Nypol® PA A3 G20 HS PRTA011 NR446
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Nypol® PA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P7v58M_Nypol-PA-A3-G20-HS-PRTA011-NR446.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide 6.6 in black color reinforced with 20% of fiberglass, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 to 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.70 to 0.90 | % | ASTM D955 |
| Water Absorption (Equilibrium) | 1.2 | % | ASTM D570 |
| Ash Content | 18 to 22 | % | ASTM D2584 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | 65 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 110 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 4.5 | % | ASTM D638 |
| Flexural Modulus | 5550 | MPa | ASTM D790 |
| Flexural Strength | 160 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 65 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 255 | °C | |
| 1.8 MPa, Unannealed | 243 | °C | |
| Melting Temperature | 250 to 265 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 19 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 70.0 to 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Adell Polyamide AR-14 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| ALCOM® AWL 15/1 UV WT1471-04LB | ALBIS PLASTIC GmbH | ABS | ALCOM® AWL |
| Celcon® M270™ | Celanese Corporation | Acetal (POM) Copolymer | Celcon® |
| HIFOR® LF1010AA | Westlake Chemical Corporation | LLDPE | HIFOR® |
| Monprene® OM-12265-01 (PRELIMINARY DATA) | Teknor Apex Company | TPE | Monprene® |