Order Products : sales@su-jiao.com
VECTRA® E440i
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | VECTRA® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P7u0Up_VECTRA-E440i.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Mineral and glass filled grade with low warp, easy flow and smooth surface apperance. Chemical abbreviation according to ISO 1043-1 : LCP Inherently flame retardant. FDA compliant |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.77 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction | 0.50 | % | ISO 294-4 |
| Flow direction | 0.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11600 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 118 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus (23°C) | 12000 | MPa | ISO 178 |
| Flexural Stress (23°C) | 165 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 6.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 24 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 9.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength (23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 1.8 MPa, not annealed | 260 | °C | ISO 75-2/A |
| 8.0 MPa, not annealed | 177 | °C | ISO 75-2/C |
| Melting Temperature 1 | 335 | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral | 2.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 - 170 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Hopper Temperature | 20.0 - 30.0 | °C | |
| Rear Temperature | 315 - 325 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 330 - 340 | °C | |
| Nozzle Temperature | 335 - 345 | °C | |
| Processing (Melt) Temp | 340 - 350 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 50.0 - 150 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 - 150 | MPa | |
| Back Pressure | 0.00 - 3.00 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 335 to 345°CZone 4 Temperature: 330 to 340°CFeed Temperature: 60 to 80°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® LD 19009 | Plastic Solutions, Inc. | LDPE | PrimaFlex® |
| Ebalta AH 140 / TC 60 | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Geon™ Vinyl Flexible A5DM0 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 83036-80C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SQUARE® LIM1550-35A/B | Shenzhen SQUARE Silicone Co., Ltd. | Silicone Rubber, LSR | SQUARE® |