ZEONEX® F52R
| Category: | COC , Cyclic Olefin Copolymer |
| Manufacturer: | Zeon Corporation |
| Trademark: | ZEONEX® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P7HrNF_ZEONEX-F52R.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ZEONEX® - Cyclo Olefin Polymer (COP) offers excellent optical properties for creating optical parts for cameras and laser beam printers. ZEONEX's high purity is suitable for a wide range of medical packaging products, while its low dielectric constant and loss tangents are appropriate for electrical insulation applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/2.16 kg) | 22 | g/10 min | ISO 1133 |
| Water Absorption (Equilibrium) | < 0.010 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Pencil Hardness | F | JIS K5401 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Injection Velocity | 30.0 to 80.0 | cm³/s | |
| Screw Speed | 20 to 60 | rpm |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3000 | MPa | ISO 527-2 |
| Tensile Stress | 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 2400 | MPa | ISO 178 |
| Flexural Stress | 109 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 19 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 144 | °C | ASTM D648 |
| Glass Transition Temperature | 156 | °C | JIS K7121 |
| CLTE - Flow | 6.0E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 1.0E+16 | ohms·cm | IEC 60093 |
| Dielectric Strength 1(1.00 mm) | 60 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 2.50 | IEC 60250 | |
| Dissipation Factor (1 MHz) | 7.0E-4 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.535 | ASTM D542 | |
| Transmittance (3000 µm) | 92.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 4.0 to 10 | hr | |
| Rear Temperature | 270 to 300 | °C | |
| Middle Temperature | 270 to 300 | °C | |
| Front Temperature | 270 to 300 | °C | |
| Mold Temperature | 105 to 150 | °C | |
| Injection Pressure | 50.0 to 180 | MPa | |
| Holding Pressure | 50.0 to 180 | MPa | |
| Back Pressure | 5.00 to 10.0 | MPa |
| Note Message | |
|---|---|
| 1 . | Method A (Short-Time) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RAYPRENE® NB221-S4042 | R&P (Pte.) Ltd. | TPE | RAYPRENE® |
| BJB Polyurethane TC-8745 A/B | BJB Enterprises, Inc. | TSU | BJB Polyurethane |
| Ducor® 2348 M | Ducor Petrochemicals BV | PP Impact Copolymer | Ducor® |
| HiFill® PA6/6 GF35 HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| Petrothene® NA202000 | LyondellBasell Industries | LDPE | Petrothene® |