Starpylen MX06023
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Starpylen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P6mffE_Starpylen-MX06023.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Starpylen MX06023 is a 20 % Milled Glass Fiber Reinforced Polypropylene Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.04 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.60 to 1.2 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2000 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 25.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | > 20 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 2300 | MPa | ISO 178 |
| Flexural Stress | 35.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 4(23°C) | 70 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength 5(23°C) | 20 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 6(23°C) | 65 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 7 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 105 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 70.0 | °C | ISO 75-2/Ae |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 195 to 205 | °C | |
| Middle Temperature | 215 to 225 | °C | |
| Front Temperature | 225 to 250 | °C | |
| Processing (Melt) Temp | 225 to 250 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 80*10*4 sp=62mm |
| 4 . | 80*10*4 sp=62mm |
| 5 . | 80*10*4 |
| 6 . | 80*10*4 |
| 7 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAIRILITE AC3610 | Formosa Plastics Corporation | PC | TAIRILITE |
| Moplen HP301R | LyondellBasell Industries | PP Homopolymer | Moplen |
| TEREZ PA 6.6 7530 GF 30 | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| Nymax™ 1308A HS BK13 | PolyOne Corporation | Nylon 66 | Nymax™ |
| Plasmer 1070B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |