RIALGLASS H 07 S 25 GT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | RIALGLASS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P6MeGo_RIALGLASS-H-07-S-25-GT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homoplymer 25% talc and glass fiber reinforced, chemically coupled; thermal stabilization of process. Flowability specific for injection molding of complex particulars; good thermal and mechanical properties. Available natural, colored or in black versions. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.1 | % | |
| Flow | 0.65 | % | |
| Ash Content | 25 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 80 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 65.0 | MPa | ISO 527-2/20 |
| Tensile Strain (Break, 23°C) | 3.0 | % | ISO 527-2/20 |
| Flexural Modulus 1(23°C) | 4500 | MPa | ISO 178 |
| Flexural Stress (23°C) | 97.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 5.5 | kJ/m² | |
| 23°C | 8.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 140 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 130 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 335 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 200 to 220 | °C | |
| Mold Temperature | 50.0 to 60.0 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene HP521-00 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| APEX® 1581 | Teknor Apex Company | PVC, Flexible | APEX® |
| Chemlon® 217 GIU | Teknor Apex Company (Chem Polymer) | Nylon 6 | Chemlon® |
| CP PRYME® Acetal AC100-9 | Chase Plastics Services Inc. | Acetal (POM) Copolymer | CP PRYME® Acetal |
| HiFill® ABS GB10 | Techmer Engineered Solutions | ABS | HiFill® |