DynaMix™ 3200-H
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | Polymer Dynamix |
| Trademark: | DynaMix™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P4gm6a_DynaMix-3200-H.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Viscosity PEEK Features:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.30 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 95.8 | MPa | |
| Break | 96.2 | MPa | |
| Tensile Elongation | ASTM D638 | ||
| Yield | 5.0 to 6.0 | % | |
| Break | 20 to 30 | % | |
| Flexural Modulus | 3720 | MPa | ASTM D790 |
| Flexural Strength | 155 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 315 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 138 to 149 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 343 to 360 | °C | |
| Middle Temperature | 357 to 371 | °C | |
| Front Temperature | 366 to 382 | °C | |
| Nozzle Temperature | 366 to 382 | °C | |
| Processing (Melt) Temp | 366 to 382 | °C | |
| Mold Temperature | 177 to 204 | °C | |
| Injection Rate | Moderate | ||
| Screw Speed | 40 to 70 | rpm | |
| Clamp Tonnage | 4.1 to 6.9 | kN/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rotec® ABS 3001 | ROMIRA GmbH | ABS | Rotec® ABS |
| Monprene® OM-16260 | Teknor Apex Company | TPE | Monprene® |
| Dynacom 501-G20 | Dynachem Co. Ltd. | ABS | Dynacom |
| LNP™ LUBRICOMP™ ZL003 compound | SABIC Innovative Plastics | PPE+PS | LNP™ LUBRICOMP™ |
| SCHULABLEND® SCHULABLEND® (ABS/PA) M/MK 7102 GF20 | A. Schulman Europe | ABS+Nylon | SCHULABLEND® |