LNP™ THERMOCOMP™ 9X11428J compound
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P4CyY0_LNP-THERMOCOMP-9X11428J-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP 9X11428J is a compound based on Polyphenylsulfone containing Proprietary Fillers. Added features of this material include: Healthcare, Low Extractable. Also known as: LNP* THERMOCOMP* Compound 9X11428J Product reorder name: 9X11428J |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.34 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.90 to 2.0 | % | |
| Across Flow : 24 hr | 1.0 to 3.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.29 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2390 | MPa | ASTM D638 |
| -- | 2330 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 74.0 | MPa | ASTM D638 |
| Yield | 71.0 | MPa | ISO 527-2/5 |
| Break 3 | 58.0 | MPa | ASTM D638 |
| Break | 57.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 8.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/5 |
| Break 5 | 15 | % | ASTM D638 |
| Break | 22 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2430 | MPa | ASTM D790 |
| -- 7 | 2270 | MPa | ISO 178 |
| Flexural Stress | 91.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 190 | J/m | ASTM D256 |
| 23°C 8 | 11 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 42.9 | J | ASTM D3763 |
| -- | 44.0 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 213 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 210 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 199 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 196 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 5.5E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 5.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 221 to 232 | °C | |
| Middle Temperature | 243 to 254 | °C | |
| Front Temperature | 260 to 271 | °C | |
| Processing (Melt) Temp | 238 to 266 | °C | |
| Mold Temperature | 82.2 to 98.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPR 12232 | TOTAL Refining & Chemicals | PP Random Copolymer | TOTAL Polypropylene |
| BMC T45HT | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Borealis PE BB2581 | Borealis AG | HDPE | Borealis PE |
| Braskem PP RP 250 | Braskem America Inc. | PP Random Copolymer | Braskem PP |
| SEQUEL® 1825 FP BLK | LyondellBasell Industries | PP, Unspecified | SEQUEL® |