Quadrant EPP CELAZOLE® PBI
| Category: | PBI , Polybenzimidazole |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P3gEAm_Quadrant-EPP-CELAZOLE-PBI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celazole® is a registered trademark of PBI Performance Products. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.30 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr, 3.00 mm | 0.50 | % | |
| Saturation, 23°C | 14 | % | |
| Water Absorption 1(23°C, 3.00 mm) | 38.0 | mg | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (E-Scale, 10.0 mm) | 105 | ISO 2039-2 | |
| Ball Indentation Hardness (10.0 mm) | 375 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1B/1 |
| Tensile Stress (Break) | 140 | MPa | ISO 527-2/1B/5 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2/1B/5 |
| Compressive Stress | ISO 604/1 | ||
| 2% Strain | 82.0 | MPa | |
| 1% Strain | 42.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 3.5 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 425 | °C | ISO 75-2/A |
| Continuous Use Temperature | |||
| -- 2 | 310 | °C | |
| -- 3 | 500 | °C | |
| Glass Transition Temperature | 425 | °C | |
| CLTE - Flow | |||
| 23 to 100°C | 2.5E-5 | cm/cm/°C | |
| 23 to 150°C | 2.5E-5 | cm/cm/°C | |
| > 150°C | 2.5E-5 | cm/cm/°C | |
| Thermal Conductivity (23°C) | 0.40 | W/m/K |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | IEC 60093 |
| Electric Strength (1.00 mm) | 22 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 3.30 | ||
| 1 MHz | 3.20 | ||
| Dissipation Factor (100 Hz) | 1.0E-3 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Oxygen Index | 58 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Weight, 24 hrs |
| 2 . | 20000 hrs |
| 3 . | Short periods |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| megol® TA 40 | API SpA | SEBS | megol® |
| SHIN-A SEB-400M80 | SHIN-A T&C | Epoxy | SHIN-A |
| Geon™ Vinyl Rigid Extrusion 87160 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Extrusion |
| Hanwha Total PP HF407 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| ICORENE® N4435 | ICO Polymers EMEA, A Division of A. Schulman | PP Homopolymer | ICORENE® |