Star L PA66 D91
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Eurostar Engineering Plastics |
| Trademark: | Star L |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P3HFh2_Star-L-PA66-D91.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Star L PA66 D91 is a PTFE lubricated, Aramid Fiber Reinforced , Polyamide 66 Injection Molding Resin |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.23 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow (4.00 mm) | 1.2 to 1.8 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 88.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 6.0 | % | ISO 527-2 |
| Flexural Modulus | 3500 | MPa | ISO 178 |
| Flexural Stress | 110 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 1(23°C) | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 2(23°C) | 35 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3 | |||
| 0.45 MPa, Unannealed, 100 mm Span | 241 | °C | ISO 75-2/Be |
| 1.8 MPa, Unannealed, 100 mm Span | 125 | °C | ISO 75-2/Ae |
| Melting Temperature (DSC) | 265 | °C | ISO 3146 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 265 to 275 | °C | |
| Middle Temperature | 270 to 280 | °C | |
| Front Temperature | 270 to 280 | °C | |
| Processing (Melt) Temp | 270 to 280 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 80*10*4 |
| 2 . | 80*10*4 |
| 3 . | 120*10*4 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PrimaFlex® ABS 556 | Plastic Solutions, Inc. | ABS | PrimaFlex® |
| Moplen EP500M | LyondellBasell Industries | PP Impact Copolymer | Moplen |
| ACCUTECH™ ABS831G20L | ACLO Compounders Inc. | ABS | ACCUTECH™ |
| Exac CTFE | Saint Gobain - Norton | PCTFE | Exac |
| Europrene Latice® 5570 | Versalis S.p.A. | SBR, Emulsion | Europrene Latice® |