EMERGE™ PC 4330-15
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P38zNS_EMERGE-PC-4330-15.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE™ PC 4330-15 Advanced Resin is a polycarbonate resin offering ultraviolet light stability, high heat resistance, and maximum toughness. This UV stable resin is available in a full range of colors that can be custom tailored to meet your product requirements. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, 3.20 mm, Injection Molded) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2410 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Yield, 3.20 mm, Injection Molded | 60.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 71.0 | MPa | |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 150 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2410 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 96.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 850 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm, Injection Molded) | No Break | ASTM D256 | |
| Instrumented Dart Impact 1(23°C, 3.20 mm, Injection Molded, Total Energy) | 87.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Annealed, 3.99 mm | 143 | °C | |
| 1.8 MPa, Unannealed, 3.99 mm | 127 | °C | |
| 1.8 MPa, Annealed, 3.99 mm | 140 | °C | |
| Vicat Softening Temperature | 148 | °C | ASTM D1525 2 |
| CLTE - Flow (-40 to 80°C) | 6.8E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 2.0E+17 | ohms·cm | ASTM D257 |
| Dielectric Strength | 17 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.00 | ||
| 1 MHz | 3.00 | ||
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 1.0E-3 | ||
| 1 MHz | 2.0E-3 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 3 | UL 94 | ||
| 1.59 mm | HB | ||
| 3.20 mm | HB | ||
| Oxygen Index 4 | 26 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | 3.39 m/sec |
| 2 . | Rate A (50°C/h), Loading 2 (50 N) |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 4 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Eltex® B6921/40N2010 | INEOS Olefins & Polymers Europe | HDPE | Eltex® |
| Karina BLACK PVC COMPOUND 951-48/4-A-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Lupolen 4261 A SW63200 | LyondellBasell Industries | HDPE, HMW | Lupolen |
| PERCOM® MCS12TR | A. Schulman Europe | PP Copolymer | PERCOM® |
| Osterlene® HB1049 | Osterman & Company | EHMWPE | Osterlene® |