Sarlink® TPV X23080N
| Category: | TPV , Thermoplastic Vulcanizate |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Sarlink® TPV |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P32vEY_Sarlink-TPV-X23080N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A highly engineered Thermoplastic Elastomer for use in demanding applications. Sarlink® X23080N is a low hardness grade possessing exceptional tensile strength, superior compression set, chemical resistance and high temperature performance. It can be easily processed by injection molding, blow molding or extrusion for various applications such as boots and bellows, seals, gaskets as well as other profiles and articles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.902 | g/cm³ | ASTM D792, ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240, ISO 868 | ||
| Shaw A, 5 seconds, extruded | 80 | ASTM D2240, ISO 868 | |
| Shore A, 5 seconds, injection molding | 84 | ASTM D2240, ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412, ISO 37 | ||
| Transverse flow : 100% strain | 4.20 | MPa | ASTM D412, ISO 37 |
| Flow : 100% strain | 7.10 | MPa | ASTM D412, ISO 37 |
| Tensile Strength | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 10.0 | MPa | ASTM D412, ISO 37 |
| Flow : Fracture | 7.70 | MPa | ASTM D412, ISO 37 |
| Tensile Elongation | ASTM D412, ISO 37 | ||
| Transverse flow : Fracture | 780 | % | ASTM D412, ISO 37 |
| Flow : Fracture | 290 | % | ASTM D412, ISO 37 |
| Tear Strength - Across Flow | |||
| -- | 47.7 | kN/m | ASTM D624 |
| -- 1 | 48 | kN/m | ISO 34-1 |
| Compression Set | ASTM D395, ISO 815 | ||
| 23°C, 22 hr | 33 | % | ASTM D395, ISO 815 |
| 70°C, 22 hr | 51 | % | ASTM D395, ISO 815 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Apparent Shear Viscosity - Capillary, @ 206/s | |||
| 200°C | 504 | Pa·s | ISO 11443 |
| 200°C | 504 | Pa·s | ASTM D3835 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 177 - 216 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 182 - 221 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Back Pressure | 0.0689 - 1.03 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Cylinder Zone 1 Temp. | 182 - 204 | °C | |
| Cylinder Zone 2 Temp. | 182 - 204 | °C | |
| Cylinder Zone 3 Temp. | 188 - 210 | °C | |
| Cylinder Zone 4 Temp. | 188 - 210 | °C | |
| Melt Temperature | 193 - 216 | °C | |
| Die Temperature | 193 - 216 | °C | |
| Take-Off Roll | 21.1 - 48.9 | °C |
| Extrusion instructions |
|---|
| Screen Pack: 20 to 60 meshScrew: 3:1 Compression Ratio |
| Note Message | |
|---|---|
| 1 . | Method B, right-angle specimen (without cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAJORIS SG300 - 8229 | AD majoris | Nylon 6 | MAJORIS |
| Radilon® S 35L 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| Vipel® F010-CNP-25 | AOC, L.L.C. | Vinyl Ester | Vipel® |
| WACKER® Catalyst T 77 | Wacker Chemie AG | Silicone | WACKER® |
| Glastic® 1401 | Bulk Molding Compounds, Inc. | Polyester, TS | Glastic® |