Polybutene-1 DP 0400M
| Category: | PB , Polybutylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Polybutene-1 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P1pOhS_Polybutene-1-DP-0400M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polybutene-1 grade DP 0400M is a semi-crystalline homopolymer, which can be used where creep, environmental stress crack resistance and elevated temperature performance are key requirements. This polymer is highly compatible with polypropylene due to its similar molecular structure. It is less compatible in blends with polyethylene but it is still easily dispersible. Its relative slow crystalliation kinetics allows for an excellent wetting behaviour. Besides its high shear sensitive flow behaviour it remains easily dispersible, also in even more incompatible polymers like thermoplastic elastomers. Foodlaw compliance information about this product can be found in separate product documentation. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 0.900 | g/cm³ | ASTM D792B |
| -- | 0.915 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | |||
| 230°C/2.16 kg | 80 | g/10 min | ASTM D1238 |
| 190°C/2.16 kg | 15 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 24.0 | MPa | ASTM D638 |
| Yield 2 | 22.0 | MPa | ISO 8986-2 |
| Break 3 | 29.0 | MPa | ISO 8986-2 |
| Tensile Elongation | |||
| Yield 4 | 4.0 | % | ASTM D638 |
| Break 5 | 300 | % | ISO 8986-2 |
| Flexural Modulus | |||
| 1% Secant 6 | 1240 | MPa | ASTM D790A |
| -- 7 | 450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 91 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 108 | °C | ASTM D648 |
| Melting Temperature | DSC | ||
| -- 8 | 114 | °C | |
| -- 9 | 126 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Conditioned 10 days at 20°C |
| 3 . | Conditioned 10 days at 20°C |
| 4 . | 51 mm/min |
| 5 . | Conditioned 10 days at 20°C |
| 6 . | 1.3 mm/min |
| 7 . | Conditioned 10 days at 20°C |
| 8 . | Tm2 |
| 9 . | Tm1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP440N | LyondellBasell Industries | PP Random Copolymer | Moplen |
| ARC ARC66G13 | ARC Resin Corporation | Nylon 66 | ARC |
| Generic Nylon 66 - Glass Fiber, Long | Generic | Nylon 66 | Generic |
| INEOS LLDPE LL6208LJ | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |
| SD POLYCA™ LD2050-AAH12 | Sumika Styron Polycarbonate Limited | PC | SD POLYCA™ |