| ESPREE™ ABS5GF is an Acrylonitrile Butadiene Styrene (ABS) product filled with 5.0% glass fiber. It can be processed by injection molding and is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 0.90 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.18 mm) | 43.1 | MPa | ASTM D638 |
| Flexural Modulus 2(3.18 mm) | 2900 | MPa | ASTM D790 |
| Flexural Strength 3(3.18 mm) | 62.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.35 mm) | 94.4 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 87.8 | °C | |
| Drying Time | 2.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 48.9 to 65.6 | °C | |
| Back Pressure | 0.345 to 1.38 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.1 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Virantage® VW-10200 RP, RFP, RSFP | Solvay Specialty Polymers | PESU | Virantage® |
| Nanguang TPU Y-90AX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| Bergamid™ A70 G50 HW Black | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Hostaform® MT12U01 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| Laprene® 8KS901A90/H | SO.F.TER. SPA | SEBS | Laprene® |