Sumikon® X6952
| Category: | Phenolic , Phenolic |
| Manufacturer: | SBHPP |
| Trademark: | Sumikon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P1L1bM_SumikonX6952.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SUMIKON® X6952 Type Black is a glass fiber reinforced phenolic molding compound with superior mechanical properties : highest impact and excellent retention of mechanical properties at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.74 | g/cm³ | JIS K6911 |
| Molding Shrinkage - Flow | 0.33 | % | JIS K6911 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 140 | MPa | JIS K6911 |
| Flexural Modulus | 18400 | MPa | JIS K6911 |
| Flexural Strength | 260 | MPa | JIS K6911 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | JIS K6911 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 220 | °C | JIS K6911 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Resistance | JIS K6911 | ||
| -- 1 | 3.0E+12 | ohms | JIS K6911 |
| -- 2 | 4.0E+11 | ohms | JIS K6911 |
| Note Message | |
|---|---|
| 1 . | As molded |
| 2 . | After boiling |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Versaflex™ CL30 | PolyOne Corporation | TPE | Versaflex™ |
| Flexane® 80 Liquid | Devcon | PUR, Unspecified | Flexane® |
| Geon™ Vinyl Flexible XV3715 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| ESTADIENE 3015 MT | Cossa Polimeri S.r.l. | ABS | ESTADIENE |
| Clyrell RC449S | LyondellBasell Industries | PP Random Copolymer | Clyrell |