Order Products : sales@su-jiao.com
GLAMIDE® T-663G30
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P15Pvl_GLAMIDE-T-663G30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GLAMIDE®T-663G30 is a polyamide 66 (nylon 66) product, which contains a 30% glass fiber reinforced material. It is available in North America. The main characteristics are: flame retardant/rated flame. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.37 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 7.0 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.20 - 0.50 | -- | % | ASTM D955 |
| 3.00 mm | 0.60 - 0.90 | -- | % | ASTM D955 |
| Water Absorption | ASTM D570 | |||
| 24 hr | 0.60 | -- | % | ASTM D570 |
| Equilibrium, 65% RH | 1.7 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 235 | 215 | MPa | ASTM D638 |
| Yield, 23°C | 195 | 145 | MPa | ASTM D638 |
| Yield, 80°C | 120 | 100 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 3.2 | 3.9 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 10800 | 9800 | MPa | ASTM D790 |
| 23°C | 8700 | 5800 | MPa | ASTM D790 |
| 80°C | 5400 | 4000 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 315 | 300 | MPa | ASTM D790 |
| Yield, 23°C | 280 | 210 | MPa | ASTM D790 |
| Yield, 80°C | 185 | 130 | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 70 | 80 | J/m | ASTM D256 |
| 23°C | 110 | 140 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 262 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 255 | -- | °C | ASTM D648 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 26 | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 4.10 | -- | ASTM D150 | |
| Arc Resistance | 100 | 92.0 | sec | ASTM D495 |
| Comparative Tracking Index | 575 | 575 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 调节后的 Volume Resistivity, ASTM D257: 1e10 to 1e11 ohm-m |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 280 - 310 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SIBUR Synthetic Rubber BR-1203 Ti Grade A | SIBUR, LLC | PBR, High Cis | SIBUR Synthetic Rubber |
| SUSTARIN® H AF | Röchling Sustaplast SE & Co. KG | Acetal (POM) Homopolymer | SUSTARIN® |
| Badamid® C70 | Bada AG | Nylon 66/6 | Badamid® |
| Hostacom ERC 198N G14008 | LyondellBasell Industries | PP Copolymer | Hostacom |
| Sylvin 9077-90 Grey 9525 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |