PENTAMID AHT GV30 H1 ungefärbt
| Category: | Nylon 46 , Polyamide 46 |
| Manufacturer: | PENTAC Polymer GmbH |
| Trademark: | PENTAMID AHT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P0UlSM_PENTAMID-AHT-GV30-H1-ungef-rbt.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Normal viscosity, high heat stabilised polyamide 4.6, easy flow, 30% glass fiber reinforced |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.50 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 7.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % | |
| Viscosity Number | 140 | -- | cm³/g | ISO 307 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness (H 961/30) | 250 | -- | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 6150 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 200 | 115 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 4.0 | 7.0 | % | ISO 527-2 |
| Flexural Modulus | 8800 | -- | MPa | ISO 178 |
| Flexural Stress | 250 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | 22 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 80 | 90 | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 290 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 290 | -- | °C | ISO 75-2/A |
| Melting Temperature | 295 | -- | °C | ISO 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Electric Strength (1.00 mm) | 30 | -- | kV/mm | IEC 60243-1 |
| Relative Permittivity (1 MHz) | 3.50 | -- | IEC 60250 | |
| Comparative Tracking Index | 300 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 1.60 mm | HB | -- | ||
| 3.20 mm | HB | -- |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA46, MHR, 16-110, GF30 | PA46, MHR, 16-110, GF30 | ISO 1874 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.11 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 295 to 320 | °C | |
| Middle Temperature | 310 to 325 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Processing (Melt) Temp | 315 | °C | |
| Mold Temperature | 100 | °C | |
| Injection Pressure | 85.0 | MPa | |
| Holding Pressure | 51.0 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.2:1.0 to 2.8:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Star L PA66 D61 | Eurostar Engineering Plastics | Nylon 66 | Star L |
| TOTAL Polyethylene Aceso® HDPE 5502 R3 | TOTAL Refining & Chemicals | HDPE | TOTAL Polyethylene |
| Kumho SBR 1712 | Korea Kumho Petrochemical Co., Ltd. | SBR, Emulsion | Kumho SBR |
| Karina GREEN PVC COMPOUND 700D40/356-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Plexiglas® Optical POQ66 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |