ResMart Ultra CoPP 4-NB
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | ResMart |
| Trademark: | ResMart Ultra |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P0U4vq_ResMart-Ultra-CoPP-4-NB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Prime, FDA high impact copolymer polypropylene that can be used for injection or extrusion applications |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 9.0 | % | ASTM D638 |
| Flexural Modulus | 965 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.18 mm) | No Break | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 73.9 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature - Desiccant Dryer | 79.4 | °C | |
| Drying Time - Desiccant Dryer | 2.0 | hr | |
| Processing (Melt) Temp | 191 to 232 | °C | |
| Mold Temperature | 32.2 to 65.6 | °C | |
| Injection Pressure | 68.9 to 103 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3099 X 99462 | RTP Company | PMP | RTP |
| Royalstat R67 | Spartech Plastics | ABS | Royalstat |
| SITRALON 18E-TF10-HK / C94150 black | SITRAPLAS GmbH | PC | SITRALON |
| VESTAKEEP® 2000UFP20 | Evonik Industries AG | PEEK | VESTAKEEP® |
| Karina BROWN PVC COMPOUND 800-36/217-A-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |