Lotryl® 35BA40
| Category: | EBA , Ethylene Butyl Acrylate Copolymer |
| Manufacturer: | Arkema |
| Trademark: | Lotryl® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OzUzt1_Lotryl-35BA40.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LOTRYL® 35BA40 is a random copolymer of Ethylene and Butyl Acrylate produced by high-pressure radicalar polymerization process. Applications Due to the high butyl acrylate content, LOTRYL® 35BA40 can be used for applications where flexibility and polarity are required. Combined with a high fluidity, LOTRYL® 35BA40 is particularly recommended for the formulation of hot melt adhesives. It can also be used as processing-aid in highly filled compounds. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ISO 1183, ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 35 to 45 | g/10 min | ASTM D1238, ISO 1133 |
| n-Butyl Acrylate Content | 33.0 to 37.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, Compression Molded) | 70 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 2.00 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break, Compression Molded) | 600 | % | ASTM D638, ISO 527-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | < 40.0 | °C | ISO 306/A, ASTM D1525 1 |
| Melting Temperature | 66.0 | °C | ISO 11357-3 |
| Ring and Ball Softening Point | 110 | °C | ASTM E28 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 150 to 170 | °C | |
| Cylinder Zone 2 Temp. | 170 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 170 | °C | |
| Die Temperature | 170 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rilsamid® AMNO MED | Arkema | Nylon 12 | Rilsamid® |
| Sekisui PVC HA-15F | Sekisui (Hong Kong) Limited | PVC, Unspecified | Sekisui PVC |
| YUNGSOX® PP 3084 | Formosa Polypropylene | PP Impact Copolymer | YUNGSOX® PP |
| ELASTOSIL® 440 | Wacker Chemie AG | Silicone | ELASTOSIL® |
| LEXAN™ BFL4000U resin | SABIC Innovative Plastics | PC | LEXAN™ |