LNP™ THERMOCOMP™ MC002 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OyhpmB_LNP-THERMOCOMP-MC002-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP MC002 is a compound based on Polypropylene resin containing 10% Carbon Fiber. Added feature of this material is: Electrically Conductive. Also known as: LNP* THERMOCOMP* Compound MC-1002 Product reorder name: MC002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- | 0.948 | g/cm³ | |
| -- | 0.950 | g/cm³ | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.70 to 1.0 | % | |
| Across Flow : 24 hr | 0.70 to 1.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.040 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.040 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11200 | MPa | ASTM D638 |
| -- | 6300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 35.6 | MPa | ASTM D638 |
| Yield | 24.0 | MPa | ISO 527-2/5 |
| Break 3 | 36.7 | MPa | ASTM D638 |
| Break | 35.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 4 | 2.5 | % | ASTM D638 |
| Break | 3.8 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 4710 | MPa | ASTM D790 |
| -- 6 | 9590 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 77.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 7 | 55.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 8 | 4.8 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 300 | J/m | ASTM D4812 |
| 23°C 9 | 26 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 11.3 | J | ASTM D3763 |
| -- | 5.12 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 10 | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 120 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 116 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 to 204 | °C | |
| Middle Temperature | 216 to 227 | °C | |
| Front Temperature | 238 to 249 | °C | |
| Processing (Melt) Temp | 227 to 249 | °C | |
| Mold Temperature | 32.2 to 48.9 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 1.3 mm/min |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 mm |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RECANYL AR36BK9503 | Jackdaw Polymers | Nylon 66 | RECANYL |
| Boltaron 3017 G2 SurPrint | Boltaron Performance Products | PVC, Rigid | Boltaron |
| InnoPlus HD2308J | PTT Global Chemical Public Company Limited | HDPE | InnoPlus |
| Sylvin 7843-70 Red 6288 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TECHNYL® C 206F NATURAL (R) | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |