LNP™ STAT-KON™ DX13315C compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OyIszL_LNP-STAT-KON-DX13315C-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP™ Stat-Kon™ DX13315C is an electrical conductive thermoplastic compound featuring electrostatic discharge (ESD) safe performance based on a unique Ultra Clean Polycarbonate (PC) resin reinforced with 15% carbon fiber. This compound provides good stiffness, dimension stability and has extremely high level of cleanliness for the most demanding applications in the Hard Disk Drive and Semiconductor industry. A unique feature of this material is its low C18-C40 hydrocarbons and this compound is manufactured using the LNP Clean Compounding Solution (CCS) technology. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (300°C/5.0 kg) | 30.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Flow : 3.20 mm | 0.10 to 0.30 | % | |
| Across Flow : 3.20 mm | 0.20 to 0.50 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 10400 | MPa | ASTM D638 |
| -- | 10600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 129 | MPa | ASTM D638 |
| Break | 130 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.7 | % | ASTM D638 |
| Break | 2.6 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| -- | 9170 | MPa | ASTM D790 |
| -- 4 | 9290 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 199 | MPa | ASTM D790 |
| -- | 203 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179/2C |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/2U |
| Notched Izod Impact (23°C) | 88 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 590 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 123 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.4E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 8.1E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 5.0E+3 to 5.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 5.0E+4 to 5.0E+6 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 110 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 250 to 280 | °C | |
| Middle Temperature | 280 to 320 | °C | |
| Front Temperature | 280 to 320 | °C | |
| Nozzle Temperature | 280 to 320 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 90.0 to 120 | °C | |
| Back Pressure | 1.00 to 5.00 | MPa | |
| Screw Speed | 30 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A1 G30 PRTA011 NR105 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Exxtral™ Performance Polyolefin BMU139 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| KOPA® KN135G15HIBL | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| Hostalen CRP 100 orange | LyondellBasell Industries | HDPE | Hostalen |
| IDI SMC E-203 | IDI Composites International | TS, Unspecified | IDI SMC |