RTP 3499-3 X 113393 A
| Category: | LCP , Liquid Crystal Polymer |
| Manufacturer: | RTP Company |
| Trademark: | RTP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OwMNLA_RTP-3499-3-X-113393-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Glass Fiber - LDS Platable |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.76 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.15 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 12400 | MPa | ASTM D638 |
| Tensile Strength | 123 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 2.0 - 3.0 | % | ASTM D638 |
| Flexural Modulus | 12400 | MPa | ASTM D790 |
| Flexural Strength | 165 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 210 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 750 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 277 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 235 | °C | ASTM D648 |
| Linear thermal expansion coefficient | ASTM E831 | ||
| Flow | 5.9E-6 | cm/cm/°C | ASTM E831 |
| Lateral | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.80 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.030 | ASTM D150 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm, ** Values per RTP Company testing.) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 149 | °C | |
| Drying Time | 8.0 | hr | |
| Dew Point | -28.9 | °C | |
| Processing (Melt) Temp | 327 - 360 | °C | |
| Mold Temperature | 65.6 - 121 | °C | |
| Injection Pressure | 82.7 - 124 | MPa |
| Injection instructions |
|---|
| The key to successfully molding this material is to start mold open cycles as soon as the screw reaches its retracted position. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| DOW™ HDPE 25055E | The Dow Chemical Company | HDPE | DOW™ HDPE |
| 3M™ Dyneon™ Fluoroelastomer MIP 8780 | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| Geon™ Fiberloc™ 80520 | PolyOne Corporation | PVC, Rigid | Geon™ Fiberloc™ |
| POLYCOMPO PP J139 | POLYCOMPO Co.,Ltd. | PP, Unspecified | POLYCOMPO PP |
| SD POLYCA™ CR3441-10G | Sumika Styron Polycarbonate Limited | PC+PBT | SD POLYCA™ |