Vydyne® 66Z
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ascend Performance Materials Operations LLC |
| Trademark: | Vydyne® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OvWccM_Vydyne-66Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vydyne 66Z is a high-viscosity PA66 resin suitable for injection-molding and extrusion applications. It is available in natural color only. Vydyne 66Z resin offers high strength, rigidity and toughness over a broad range of demanding applications and good fluid resistance to a wide variety of chemicals, solvents and oils. Typical Applications/End Uses: Typical uses include packaging films, monofilaments, bristles, rods, tubing, sheet and extruded profiles. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.14 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 23°C, 2.00mm | 2.1 | -- | % | ISO 294-4 |
| Flow direction : 23°C, 2.00mm | 2.2 | -- | % | ISO 294-4 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 8.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 2.5 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2850 | 1900 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | |||
| Yield, 23°C | 85.0 | 55.0 | MPa | ISO 527-2 |
| Fracture, 23°C | 55.0 | 70.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 5.0 | 20 | % | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 40 | 250 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2400 | 750 | MPa | ISO 178 |
| Flexural Strength (23°C) | 80.0 | 20.0 | MPa | ISO 178 |
| Poisson's Ratio | 0.40 | -- | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 6.0 | 6.0 | kJ/m² | ISO 179/1eA |
| 23°C | 7.0 | 30 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ISO 179/1eU | |
| 23°C | No Break | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180 | |||
| -30°C | 6.0 | 6.0 | kJ/m² | ISO 180 |
| 23°C | 7.0 | 30 | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 200 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature | 260 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow : 23 to 55°C, 2.00mm | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 55°C, 2.00mm | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Extrusion | Dry | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 250 - 295 | °C | |
| Cylinder Zone 2 Temp. | 250 - 295 | °C | |
| Cylinder Zone 3 Temp. | 250 - 295 | °C | |
| Cylinder Zone 4 Temp. | 250 - 295 | °C | |
| Cylinder Zone 5 Temp. | 250 - 295 | °C | |
| Melt Temperature | 270 - 295 | °C | |
| Die Temperature | 270 - 295 | °C |
| Extrusion instructions |
|---|
| Recommended Extrusion Conditions:Melt Point: 260°CMelt Pressure: 3 to 17 MPaBlow Film Bath Temperature: 20°C to 80°CChill Roll Temperature (Cast Film): 20°C to 80°CScrew Design: General Purpose or Barrier |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mold Max® XLS II | Smooth-On, Inc | Silicone | Mold Max® |
| Wellamid® 42LN2-N | Wellman Engineering Resins | Nylon 6 | Wellamid® |
| Epoxies, Ect. 20-3004 LV | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| MARPOL® EVA 1820 | Marco Polo International, Inc. | EVA | MARPOL® EVA |
| RELENE® HD53TA010 | Reliance Industries Limited | HDPE | RELENE® |