Softflex® 5500
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Network Polymers, Inc. |
| Trademark: | Softflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OuMtfa_Softflex-5500.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Softflex 5500 is suitable for overmolding polypropylene and polyethylene. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.918 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (235°C/1.0 kg) | 0.20 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 3.18 mm | 1.7 | % | |
| Across Flow : 3.18 mm | 1.3 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 55 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 6.14 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 1000 | % | ASTM D412 |
| Tear Strength | 27.5 | kN/m | ASTM D624 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Suggested Max Regrind | 50 | % | |
| Rear Temperature | 171 to 182 | °C | |
| Middle Temperature | 188 to 199 | °C | |
| Front Temperature | 204 to 216 | °C | |
| Nozzle Temperature | 202 to 213 | °C | |
| Mold Temperature | 21.1 to 43.3 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.621 to 1.21 | MPa | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 1.5:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TES J-50/30 BK223 | Techmer Engineered Solutions | PC | TES |
| Catalyst CT/2-HP | Solvay Specialty Polymers | Polyolefin, Unspecified | Catalyst |
| CERTENE™ HI-255 | Muehlstein | HDPE | CERTENE™ |
| Europrene® SOL T 161B | Versalis S.p.A. | SBS | Europrene® |
| Elastollan® R 2000 | BASF Polyurethanes GmbH | TPU-Polyester | Elastollan® |