| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Asahi Kasei Plastics North America Inc. |
| Trademark: | Thermylene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OuHHOa_Thermylene-P1-35FM-Y942.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
|
PP-GF+MD 35% Glass Fiber / Mineral Co-Reinforcement |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 72.0 | MPa | ISO 527-2 |
| Flexural Modulus | 6300 | MPa | ISO 178 |
| Flexural Stress | 112 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.5 | kJ/m² | ISO 179 |
| Notched Izod Impact Strength | 8.0 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 142 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 140 | °C | ISO 75-2/A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Clariant Nylon 6/6 6601-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| DAI-EL™ G-755CBP | DAIKIN AMERICA, INC. | Fluorelastomer | DAI-EL™ |
| Edgetek™ XT XT-100-BU03 Black | PolyOne Corporation | PC+PBT | Edgetek™ XT |
| Geon™ Vinyl Flexible 83700 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| Sylvin 9077-90 Grey 930 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |