ISPLEN® PP 080 A
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | REPSOL |
| Trademark: | ISPLEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OtgtGA_ISPLEN-PP-080-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene homopolymer with high melt flow rate for injection applications. ISPLEN® PP 080 A shows a high stiffness and a low warpage shrinkage behaviour. This product is standard stabilised and also antistatic formulated. APPLICATIONS
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 20 | g/10 min | ISO 1133 |
| Molding Shrinkage 1 | 1.2 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 28.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 14 | % | ISO 527-2 |
| Flexural Modulus | 1300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 1.5 | kJ/m² | |
| -20°C | 1.6 | kJ/m² | |
| 0°C | 1.6 | kJ/m² | |
| 23°C | 2.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | 14 | kJ/m² | |
| -20°C | 14 | kJ/m² | |
| 0°C | 18 | kJ/m² | |
| 23°C | 81 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | ||
| 0°C | 2.5 | kJ/m² | |
| 23°C | 2.6 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180 | ||
| 0°C | 20 | kJ/m² | |
| 23°C | 60 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 81.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 71.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 152 | °C | ISO 306/A120 |
| -- | 56.0 | °C | ISO 306/B120 |
| Note Message | |
|---|---|
| 1 . | 150x100x3mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA A3 G8 NTLA010 NR403 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| CP PRYME® PC/ABS PCA100 | Chase Plastics Services Inc. | PC+ABS | CP PRYME® PC/ABS |
| Formolene® L62009E2 | Formosa Plastics Corporation, U.S.A. | LLDPE | Formolene® |
| Latimass 82-06 D030 | LATI S.p.A. | Nylon 12 | Latimass |
| NYLOY® MS-0200N-3-H | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |