LEXAN™ EXL8414 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OswsM4_LEXANEXL8414resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LEXAN EXL8414 is a PC/siloxane copolymer resin with medium flow, excellent low temperature impact and 25% post consumer recycle content. Limited availability and restricted color only. Higher color variability and contamination risks including black specs needs to be considered before approval for use in applications. |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.18 | g/cm³ | ASTM D792 |
| -- | 1.19 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 9.2 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (300°C/1.2 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Transverse flow : 3.20mm | 0.40 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.35 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.15 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2150 | MPa | ASTM D638 |
| -- | 2360 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 57.0 | MPa | ASTM D638 |
| Yield | 57.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 60.0 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/50 |
| Fracture 5 | 110 | % | ASTM D638 |
| Fracture | 110 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2210 | MPa | ASTM D790 |
| -- 7 | 2170 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 86.0 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 91.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 82 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 740 | J/m | ASTM D256 |
| 23°C | 850 | J/m | ASTM D256 |
| -30°C 10 | 56 | kJ/m² | ISO 180/1A |
| 23°C 11 | 67 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 71.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 138 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 12 | 138 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 126 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 13 | 126 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525, ISO 306/B50 11 14 |
| -- | 145 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 6.4E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 7.2E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 6.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 7.6E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.750 mm) | HB | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.800 mm | 850 | °C | IEC 60695-2-12 |
| 1.00 mm | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 875 | °C | IEC 60695-2-13 |
| 3.00 mm | 875 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 271 - 293 | °C | |
| Middle Temperature | 282 - 304 | °C | |
| Front Temperature | 293 - 316 | °C | |
| Nozzle Temperature | 288 - 310 | °C | |
| Processing (Melt) Temp | 293 - 316 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 120*10*4 mm |
| 13 . | 120*10*4 mm |
| 14 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| WELLAMID Nylon 6600 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 66 | WELLAMID Nylon |
| 3M™ Dyneon™ PTFE TF 9201Z | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Axiall PVC 12820 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| INSPIRE™ 361 | Braskem Europe GmbH | PP, Unspecified | INSPIRE™ |
| POLYfill PP CQX10030E10 | Polykemi AB | PP, Unspecified | POLYfill |