BESTPOLUX PCU/01
| Category: | PC , Polycarbonate |
| Manufacturer: | Triesa Plastics |
| Trademark: | BESTPOLUX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OpZhyG_BESTPOLUX-PCU-01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate, Standard Grade, Low Viscosity, Lubricated and UV Stabilized for Injection Molding Grade |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 19 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.60 | % | ISO 294-4 |
| Water Absorption (23°C, 24 hr) | 0.24 | % | ISO 62 |
| Humidity - Pellets | 0.20 | % | ISO 1110 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2300 | MPa | ISO 527-2 |
| Tensile Stress | 66.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 90 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 20 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -40°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 145 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+15 | ohms | IEC 60093 |
| Electric Strength | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | 250 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate | < 100 | mm/min | FMVSS 302 |
| Flame Rating | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 260 to 280 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds PP-5342-9000 | Ravago Manufacturing Americas, LLC | PP Homopolymer | Ravago Compounds |
| Miflon® 3223 | Jiangsu Meilan Chemical Co., Ltd. | PTFE | Miflon® |
| HANWHA P-1300 | Hanwha Chemical | PVC, Unspecified | HANWHA |
| Sylvin 5210-75 Green 3187 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| POCAN® BF 4232 000000 | LANXESS Asia/Pacific | PBT | POCAN® |