Tecotek® PC50 GR10 GR053 FA20
| Category: | PC , Polycarbonate |
| Manufacturer: | Eurotec Engineering Plastics |
| Trademark: | Tecotek® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OnGpg1_Tecotek-PC50-GR10-GR053-FA20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PC, 10% glass fiber reinforced, flame retardant - halogen (RoHS compliant), grey RAL 9002 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.29 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow | 0.50 | % | |
| Flow | 0.50 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.20 | % | ISO 62 |
| Moisture Content | < 0.10 | % | ISO 15512 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Back Pressure | Low |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 4000 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 80.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 9.0 | kJ/m² | |
| 23°C | 11 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 130 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 140 | °C | ISO 306/B |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index (Solution A) | 175 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.60 mm | V-0 | ||
| Glow Wire Flammability Index (2.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 900 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 80.0 to 100 | °C | |
| Injection Rate | Moderate-Fast | ||
| Holding Pressure | 60.0 to 120 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| AMTOPP TP50 | Inteplast Group | PP, Unspecified | AMTOPP |
| Chiao Fu PA66 MD212G43 NAT | Chiao Fu Enterprises Co., Ltd. | Nylon 66 | Chiao Fu PA66 |
| Hifax CA45G | LyondellBasell Industries | TPO (POE) | Hifax |
| LNP™ THERMOCOMP™ JF006 compound | SABIC Innovative Plastics Europe | PESU | LNP™ THERMOCOMP™ |
| Sylvin 8498-72 Natural | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |