Desmopan® 786 S
| Category: | TPU, Unspecified , Thermoplastic Polyurethane Elastomer |
| Manufacturer: | Covestro - PUR |
| Trademark: | Desmopan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Omw2RQ_Desmopan-786-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| injection molding grade; very good hydrolysis and microbial resistance; high mechanical strength; good low-temperature flexibility; Application; Toys; Technical parts |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1150 | kg/m³ | ISO 1183 1 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 2 | ||
| Shore A, 3 sec | 86 | ||
| Shore D, 15 sec | 33 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 3 | DIN 53504 | ||
| Break | 38.0 | MPa | |
| 10% Strain | 2.00 | MPa | |
| 50% Strain | 5.30 | MPa | |
| 100% Strain | 7.20 | MPa | |
| 300% Strain | 13.3 | MPa | |
| Tensile Strain 4(Break) | 590 | % | DIN 53504 |
| Abrasion Resistance (23°C) | 40.0 | mm³ | ISO 4649-A |
| Tensile Storage Modulus | ISO 6721-1,-4 | ||
| -20°C | 400 | MPa | |
| 20°C | 35.0 | MPa | |
| 60°C | 20.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Resilience | 32 | % | ISO 4662 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength 5 | 60 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 30 | % | |
| 70°C, 24 hr | 65 | % |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 80.0 | °C | |
| Processing (Melt) Temp | 210 to 230 | °C | |
| Mold Temperature | 20.0 to 40.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | 200 mm/min |
| 4 . | 200 mm/min |
| 5 . | 500 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® A9960C | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Radilon® A HSX 100 NAT | Radici Plastics | Nylon 66 | Radilon® |
| StarMediflex P 7080-1000 | STAR Thermoplastic Alloys & Rubbers, Inc. | TPE | StarMediflex |
| TOPAS® 6017S-04 | Topas Advanced Polymers, Inc. | COC | TOPAS® |
| INSTRUC PPGB30 | Infinity LTL Engineered Compounds | PP, Unspecified | INSTRUC |