Plexiglas® Frosted V045-68177
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Altuglas International of Arkema Inc. |
| Trademark: | Plexiglas® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OlhSCL_Plexiglas-Frosted-V045-68177.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexiglas® Frosted V045-68177 is a Polymethyl Methacrylate Acrylic product. It is available in North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 1.8 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 to 0.80 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.40 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 94 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3230 | MPa | ASTM D638 |
| Tensile Strength (Break) | 71.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.8 | % | ASTM D638 |
| Flexural Modulus | 3240 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 106 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 16 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1 | ASTM D648 | ||
| 0.45 MPa, Annealed | 94.4 | °C | |
| 1.8 MPa, Annealed | 92.8 | °C | |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ASTM D1525 2 |
| -- | 97.2 | °C | ASTM D1525 3 |
| Thermal Conductivity | 0.19 | W/m/K | ASTM C177 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (3180 µm) | 85.0 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ASTM Classification | PMMA 0131T1V1 | ASTM D788 |
| Note Message | |
|---|---|
| 1 . | Annealing cycle: 4hrs @ 176°F |
| 2 . | Rate A (50°C/h), Loading 1 (10 N) |
| 3 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen Q30G | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| Tislamid® PA66 PA66 25 GFR FR HF | Tisan | Nylon 66 | Tislamid® PA66 |
| Celstran® PP-GF30-23 AF 3001 Natural | Celanese Corporation | PP, Unspecified | Celstran® |
| Elastron® G G101.A50.N.E | Elastron USA, Inc. | SEBS | Elastron® G |
| LNP™ STAT-KON™ DX05499 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |