EMDA-6147 is a high density polyethylene copolymer resin designed for blow molding of large size containers. Its high molecular weight and broad molecular weight distribution with a balanced density provide excellent moldability, toughness and stress-cracking resistance. The molded articles exhibit good surface attributes. EMDA-6147 is suitable for blow molding of closed head shipping containers of up to 50 liter size, fuel tanks, drums, jerry cans and other similar parts. The molded parts have smooth surfaces that can be readily treated for high quality printing. The containers may be utilized for packaging a variety of aggressive materials, such as, industrial chemicals, latex paint, printing inks and adhesives. Foodstuff can also be packaged in the containers in line with conformity of the resin with food contact regulations. EMDA-6147 is also suitable for making non-pressure "gravity" pipes for drainage and sewage applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.952 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.070 | g/10 min | |
| 190°C/21.6 kg | 9.0 | g/10 min | |
| Environmental Stress-Cracking Resistance (50°C, 10% Igepal, F50) | 1000 | hr | ASTM D1693B |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.0 | MPa | |
| Break | 35.0 | MPa | |
| Tensile Elongation (Break) | > 750 | % | ASTM D638 |
| Flexural Modulus | 1180 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Area) | 17.0 | kJ/m² | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 125 | °C | ASTM D1525 |
| Melting Temperature | 131 | °C | Internal Method |
| Peak Crystallization Temperature (DSC) | 116 | °C | Internal Method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 204 | °C | |
| Cylinder Zone 2 Temp. | 204 | °C | |
| Cylinder Zone 3 Temp. | 204 | °C | |
| Cylinder Zone 4 Temp. | 204 | °C | |
| Melt Temperature | 210 | °C | |
| Die Temperature | 204 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene GC45P200-01UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Starpylen M1000-BK1A987 | Eurostar Engineering Plastics | PP, Unspecified | Starpylen |
| Vi-Chem PVC VNC110E | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| UMG ALLOY® CV200 | UMG ABS, Ltd. | PC+ABS | UMG ALLOY® |
| Formolene® 3302B | Formosa Plastics Corporation, U.S.A. | PP Random Copolymer | Formolene® |