MBA PP 2182
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | MBA Polymers |
| Trademark: | MBA PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OkQfAk_MBA-PP-2182.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A post-consumer recycled polypropylene copolymer with a very high melt flow rate for injection moulding applications. Available in standard black (reference 90/04). |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | Internal method |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 35 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 16.5 | MPa | ISO 527-2/50 |
| Flexural Modulus (23°C) | 850 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.5 | kJ/m² | ISO 180/1A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Processing (Melt) Temp | 190 - 220 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 1.0 - 2.0 | hr | |
| Suggested Max Moisture | 0.050 - 0.10 | % | |
| Melt Temperature | 180 - 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nanofluor® Y75N | Precision Polymer Engineering Ltd. | Fluorelastomer | Nanofluor® |
| Karina GRAY PVC COMPOUND -E 835-18/115-C-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| neogol® 90 P UG | API SpA | TPO (POE) | neogol® |
| Sumiliteresin® PR-13349 | SBHPP | Phenolic | Sumiliteresin® |
| LNP™ LUBRICOMP™ RFL16 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |