Hifax TRC 103P R1K3
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hifax |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OkM5MO_Hifax-TRC-103P-R1K3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hifax TRC 103P is a mineral filled high impact polypropylene copolymer. The grade has been specifically designed for moulding large complex parts that require high impact as well as good stiffness. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.02 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 23 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.60 to 0.80 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | > 45 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 16.5 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | > 75 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 1250 | MPa | ISO 178 |
| Flexural Stress (23°C) | 19.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C | 5.0 | kJ/m² | |
| 23°C | > 20 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | > 95.0 | °C | ISO 75-2/B |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAG® 6475 | A. Schulman Europe | PBT | POLYMAG® |
| Ferro PP TPP30AE39BK | Ferro Corporation | PP Homopolymer | Ferro PP |
| EPO-TEK® OG142-112 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Karina BLACK PVC COMPOUND 800-48/ 1-E-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| POLYasa 1614F | Polykemi AB | ASA | POLYasa |