VENYL UE037 - 8139
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OhY0Ea_VENYL-UE037---8139.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL UE037 - 8139 is an unreinforced polyamide 66 with improved impact resistance intended for Injection moulding. APPLICATIONS VENYL UE037 - 8139 has been developed especially for very demanding applications in automotive industry and electrical parts requiring excellent combination between rigidity and high impact resistance at room temperature. It allows to avoid the conditioning of the part before use (low moisture absorption). VENYL UE037 - 8139 is available in both natural and other colours can be provided on request. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.10 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | 1.6 to 2.3 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 2.2 to 2.4 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2400 | 1350 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 50.0 to 55.0 | 40.0 to 45.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 13 to 45 | 170 to 220 | % | ISO 527-2 |
| Flexural Modulus | 1700 to 1900 | 900 to 1000 | MPa | ISO 178 |
| Flexural Stress | 60.0 to 70.0 | 30.0 to 40.0 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 80 to 85 | 100 to 110 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | No Break | No Break | ISO 179 | |
| Notched Izod Impact | 75 to 80 | 90 to 100 | J/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 213 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 70.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 256 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+14 | 1.0E+12 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+15 | 1.0E+12 | ohms·cm | DIN 53482 |
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 | |
| Oxygen Index | 22 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 to 285 | °C | |
| Middle Temperature | 265 to 280 | °C | |
| Front Temperature | 260 to 275 | °C | |
| Nozzle Temperature | 260 to 275 | °C | |
| Mold Temperature | 75.0 to 85.0 | °C | |
| Injection Pressure | 60.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 35.0 to 60.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 282 | RTP Company | Nylon 66 | RTP |
| Karina IVORY PVC COMPOUND 650-35/1-F | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| ADVANCENE™ EM-3405-UVH | ETHYDCO | MDPE | ADVANCENE™ |
| Dow Corning® QP1-260 | Dow Corning Corporation | Silicone | Dow Corning® |
| Innova R 770E | Videolar-Innova S/A | PS (HIPS) | Innova |