Adflex Q 108 F
| Category: | TPO (POE) , Thermoplastic Polyolefin Elastomer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Adflex |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OhHTSg_AdflexQ108F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Adflex Q 108 F is a reactor TPO (thermoplastic polyolefin) manufactured using LyondellBasell's proprietary Catalloy process technology. It is suitable for the extrusion and calendering of soft film and sheet, for the impact modification of polypropylene and other compounding applications, as well as monolayer and multilayer air quenched blown films. It is also used by our customers for automotive color-matched interior trim applications. The grade is available in natural pellet form and has no slip or antiblock, and only minimal stabilization in order to allow wider design latitude for the compounder. Additional suitable stabilization is recommended to protect the resin during melt processing and throughout its useful life. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.880 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 0.60 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 30 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 11.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | > 500 | % | ISO 527-2 |
| Flexural Modulus | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ISO 180/1A | ||
| -40°C, partial fracture | 6.0 | kJ/m² | ISO 180/1A |
| -20°C | No Break | ISO 180/1A | |
| 23°C | No Break | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 40.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 60.0 | °C | ISO 306/A50 |
| Melting Temperature | 142 | °C | ISO 11357-3 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Makrolon® Rx2530 | Covestro - Polycarbonates | PC | Makrolon® |
| Mineralblend® PP-1850 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | PP Copolymer | Mineralblend® |
| Petrothene® LP510031 | LyondellBasell Industries | HDPE | Petrothene® |
| LNP™ COLORCOMP™ MG94C compound | SABIC Innovative Plastics | ABS | LNP™ COLORCOMP™ |
| LNP™ LUBRICOMP™ AL002 compound | SABIC Innovative Plastics | ABS | LNP™ LUBRICOMP™ |