NEOFLON™ EFEP RP-5000

Category:	Fluoropolymer , Fluoropolymer
Manufacturer:	DAIKIN AMERICA, INC.
Trademark:	NEOFLON™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OhDU7d_NEOFLON-EFEP-RP-5000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

EFEP RP-5000 is a fluoropolymer combining the excellent physical and chemical properties derived from ETFE together with a low processing temperature that is more compatible with engineering resins and conventional thermoplastic polymers. This resin adheres well to many kinds of plastics and inorganic materials (glass, metals) without adhesive or etching.

EFEP RP-5000 can be easily co-extruded into multi-layer tubing or films and offers the following advantages for a wide range of applications found in the automotive, oil and gas, chemical processing, semiconductor and film industries:

Very good permeation resistance to hydrocarbons

Excellent chemical resistance

High purity

Improved heat aging resistance

Co-extrusion with other resins (nylons, EVOH, modified PE, and ETFE) without adhesive or etching

Superior adhesion strength

Excellent weathering

Cold impact resistance

General Information
Features	High purity Good heat aging resistance Good adhesion Low temperature impact resistance Good chemical resistance Good weather resistance Hydrocarbon resistance
Uses	Semiconductor molding compound Films Multilayer film Pipe fittings Application in Automobile Field
Forms	Particle
Processing Method	Co-extrusion molding Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.74	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (265°C/5.0 kg)	20 - 30	g/10 min	ASTM D1238

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	36.0 - 56.0	MPa	ASTM D638
Tensile Elongation (Break)	360 - 520	%	ASTM D638
Flexural Modulus	1000	MPa	ASTM D790

Thermal	Nominal Value	Unit	Test Method
Melting Temperature	195	°C	DSC

Additional Information	Nominal Value	Unit
Permeation Resistance - Average
60°C ¹	2.0	g·mm/m²/atm/24 hr
60°C ²	6.5	g·mm/m²/atm/24 hr

Injection	Nominal Value	Unit
Rear Temperature	200 - 220	°C
Middle Temperature	220 - 240	°C
Front Temperature	250 - 270	°C
Nozzle Temperature	250 - 270	°C
Mold Temperature	30.0 - 100	°C
Injection Pressure	50.0 - 100	MPa

Injection instructions
Injection Speed: 3-15 mm/sCooling Time: 10-40 sec

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	260	°C
Cylinder Zone 3 Temp.	260	°C
Cylinder Zone 5 Temp.	260	°C
Adapter Temperature	265	°C
Die Temperature	280	°C

Extrusion instructions
Cylinder Diameter: 30 mmScrew L/D: 24Compression Ratio: 3Die I.D.: 16 mmTip O.D.: 12 mm

Note Message
1 .	100% Methanol
2 .	CE-10

Resin Grade	Manufacturer	Category	Trademark
Rigidex® HD5502S	INEOS Olefins & Polymers Europe	HDPE, MMW	Rigidex®
Tecopet® PT70 GR15 NL100 PS20	Eurotec Engineering Plastics	PET	Tecopet®
Trexprene® A74BW	Mitsubishi Chemical Performance Polymers, Inc.	TPV	Trexprene®
HiFill® PA6 GB30 L	Techmer Engineered Solutions	Nylon 6	HiFill®
Infino NH-1017SG	LOTTE ADVANCED MATERIALS CO., LTD.	PC+ABS	Infino