Strippable Semiconductive Shielding E8551 is a crosslinkable, strippable semiconductive compound, designed for both XLPE and EPDM rubber insulated cables and use in both dry and steam curing processes. Specifications: E8551 meets the requirements as below, when optimal processing extrusion and end testing procedure are used: AEIC CS8 (latest edition) BS 6622 IEC 60502 NF C 33-223 NEMA WC 7-1996/ICEA S-95-658 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.18 | g/cm³ | ASTM D1928 |
| Mooney Viscosity (ML 1+4, 121°C) | 19 | MU | ISO 289 |
| Moisture Content 1 | ppm | Internal method |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermosetting (200°C) 2 | 60/20 | % | IEC 60540 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Stripping Angle | 180 | ° | |
| Stripping Force 3 | |||
| EPR : 23°C | 1.5 - 2.0 | kN/m | |
| XPLPE : 23°C | 0.7 - 1.0 | kN/m |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 85 - 90 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 11.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 220 | % | ASTM D638 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (135°C, 168 hr) | -10 | % | ASTM D471 |
| Change in Ultimate Elongation (135°C, 168 hr) | -30 | % | ASTM D471 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | ASTM D257 | ||
| 23°C | < 5.0E+2 | ohms·cm | ASTM D257 |
| 90°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| 120°C | < 1.0E+3 | ohms·cm | ASTM D257 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | < 40.0 | °C | |
| Cylinder Zone 1 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 2 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 3 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 4 Temp. | 60.0 - 110 | °C | |
| Cylinder Zone 5 Temp. | 60.0 - 110 | °C | |
| Die Temperature | 100 - 130 | °C |
| Extrusion instructions |
|---|
| Neck Temperature: 100 to 130°CHead Temperature: 100 to 130°C |
| Note Message | |
|---|---|
| 1 . | QAHC-10420 (Karl Fischer method) |
| 2 . | 20 N/cm² |
| 3 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 202 TFE 10 HS | RTP Company | Nylon 66 | RTP |
| Next Nylon 66 Industrial Series PX-02BK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Industrial Series |
| DOMAMID® 66G50HR | DOMO Engineering Plastics SPA | Nylon 66 | DOMAMID® |
| Eco-Solutions GP82W | MINIMA Technoloy Co. Ltd. | Biodeg Polymers | Eco-Solutions |
| KOPLA PA66 KDG1080 | KOPLA Co., Ltd. | Nylon 66 | KOPLA PA66 |