| 35% Glass Reinforced, Heat Stabilized, Hydrolysis Resistant, Polyamide 66 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.1 | -- | % | |
| Flow | 0.40 | -- | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr, 2.00 mm | 5.5 | -- | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 1.7 | -- | % | |
| Viscosity Number | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 11000 | 8000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 210 | 140 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | 5.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 7400 | MPa | |
| 1000 hr | -- | 5000 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 15 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | 75 | kJ/m² | |
| 23°C | 80 | 95 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 14 | 16 | kJ/m² | ISO 180/1A |
| Multi-Axial Instrumented Impact Energy (23°C) | 6.00 | -- | J | ISO 6603-2 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 255 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/A |
| Glass Transition Temperature 1 | 80.0 | -- | °C | ISO 11357-2 |
| Vicat Softening Temperature | 255 | -- | °C | ISO 306/B50 |
| Melting Temperature 2 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.7E-5 | -- | cm/cm/°C | |
| Transverse | 8.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+13 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate (1.00 mm) | 18 | -- | mm/min | ISO 3795 |
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.700 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 21 | -- | % | ISO 4589-2 |
| Fill Analysis | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melt Density | 1.27 | -- | g/cm³ | |
| Specific Heat Capacity of Melt | 2300 | -- | J/kg/°C | |
| Thermal Conductivity of Melt | 0.22 | -- | W/m/K |
| Additional Information | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Odor | 4 | -- | VDA 270 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Edgetek™ PK-30GF/000 NC | PolyOne Corporation | PEEK | Edgetek™ |
| GLS PP YN06 MH1 | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| Elastron® G G400.A52.T | Elastron USA, Inc. | SEBS | Elastron® G |
| HI-ZEX™ 8000F | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| Deprene 103-50 | Shanghai Lin Gen Rubber Materials Co., Ltd. | PP+EPDM | Deprene |