LG PS 15NFI
| Category: | PS (GPPS) , General Purpose Polystyrene |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | LG PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Oetpoe_LG-PS-15NFI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description High Transparency, Heat Resistance Application Food Container, Merchandise, Artificial Woods, Refrigerator Vegetable Box, PSP, Sheet, Film, etc. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 10 | g/10 min | |
| 220°C/10.0 kg | 120 | g/10 min | |
| 230°C/3.8 kg | 28 | g/10 min | |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2850 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 46.1 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 4.0 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 3260 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 84.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 6.40 mm | 9.8 | J/m | |
| 23°C, 6.40 mm | 9.8 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 6.40 mm | 93.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 87.0 | °C | |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 6 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.010 | % | |
| Rear Temperature | 170 to 190 | °C | |
| Middle Temperature | 180 to 200 | °C | |
| Front Temperature | 190 to 210 | °C | |
| Nozzle Temperature | 190 to 220 | °C | |
| Processing (Melt) Temp | 190 to 220 | °C | |
| Mold Temperature | 40.0 to 70.0 | °C | |
| Back Pressure | 29.4 to 58.8 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ResMart Ultra CoPP 20-2 | ResMart | PP Impact Copolymer | ResMart Ultra |
| Aristech ALTAIR PLUS® (0.160 inch) | Aristech Acrylics LLC | ABS+Acrylic | Aristech |
| LG PVC LB100M | LG Chem Ltd. | PVC, Unspecified | LG PVC |
| Karina WHITE PVC COMPOUND -E 854-10/185-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PLUSTEK PA517 | Polyram Ram-On Industries | Nylon 66/6 | PLUSTEK |