Westlake LLDPE LF2018
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Westlake Chemical Corporation |
| Trademark: | Westlake LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OeAPIg_Westlake-LLDPE-LF2018.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Westlake LF2018 is a hexene LLDPE suitable for heavy duty films and shipping sacks. This material has increased stiffness, and can be blended with LDPE for strength property enhancements. Application/Uses: Heavy duty bags and sacks Agricultural films |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 283 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 372 | MPa | ASTM D882 |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 42.1 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 37.2 | MPa | ASTM D882 |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 1100 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 1100 | % | ASTM D882 |
| Dart Drop Impact 4(25 µm, Blown Film) | 300 | g | ASTM D1709 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (25.4 µm, Blown Film) | 15 | % | ASTM D1003 |
| Additional Information |
|---|
| Test specimens for blown film: nominal thickness 1.0 mils fabricated at 2.5:1 BUR. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 216 | °C |
| Note Message | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | Test run at 23°C (73°F) and 50% relative humidity |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PPR PPHO02 | Premier Plastic Resins, Inc. | PP Homopolymer | PPR |
| Sylvin 9909-65 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Ecodear® V751X53 | Toray Resin Company | PLA | Ecodear® |
| Karina SANDALWOOD PVC COMP. -E 856-08/471-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |
| Sylvin 3240-65 Red 683 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |