PC 5025IR polycarbonate resin offers superior mechanical properties, good dimensional stability and high electrical performance, allowing it to be widely used for electrical, electronic, appliance, automotive and optical industries. PC 5025IR is a polycarbonate resin grade which has high low temperature impact strength in combination with superior mechanical and physical property.

CHARACTERISTICS

Superior low temperature impact resistance

Workable under a wide range of temperatures

Good dimensional stability

Good weather resistance

Good flow-ability

High electrical performance

Low moisture absorbency

APPLICATIONS

PC 5025IR resin grade is used for electric and electronic applications, food contact material and etc.

Medium viscosity. Transparent colors only.

General Information
Features	Good dimensional stability Low hygroscopicity Good electrical performance Good liquidity Low temperature impact resistance Good weather resistance Compliance of Food Exposure Medium viscosity
Uses	Electrical/Electronic Applications Non-specific food applications Optical applications Home appliance components Application in Automobile Field
Appearance	Clear/transparent
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.20	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (220°C/10.0 kg)	10	g/10 min	ASTM D1238
Molding Shrinkage - Flow	0.50 - 0.70	%	ASTM D955
Water Absorption (Equilibrium)	0.15	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (Yield)	70.3	MPa	ASTM D638
Tensile Elongation (Break)	120	%	ASTM D638
Flexural Modulus	2060	MPa	ASTM D790
Flexural Strength (Yield)	86.2	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (23°C, 3.18 mm)	910	J/m	ASTM D256

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	135	°C	ASTM D648
CLTE - Flow	5.0E-5 - 7.0E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	4.0E+16	ohms·cm	ASTM D257
Dielectric Strength	30	kV/mm	ASTM D149
Arc Resistance	120	sec	ASTM D495

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.6 mm)	V-2		UL 94

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	3.0 - 5.0	hr
Suggested Max Moisture	0.020	%
Rear Temperature	245 - 270	°C
Middle Temperature	260 - 285	°C
Front Temperature	275 - 300	°C
Nozzle Temperature	275 - 310	°C
Processing (Melt) Temp	275 - 310	°C
Mold Temperature	65 - 105	°C
Back Pressure	0.250 - 0.703	MPa
Screw Speed	40 - 70	rpm
Vent Depth	0.020 - 0.079	mm

Resin Grade	Manufacturer	Category	Trademark
MIDILENA III PPJ900	ROMPETROL PETROCHEMICALS S.R.L.	PP Homopolymer	MIDILENA III
TRIREX® 3022L1(S2)	Samyang Corporation	PC	TRIREX®
Galloo GP-PP-157	Galloo Plastics	PP, Unspecified	Galloo
Elastron® G G501.A35.N.PS	Elastron USA, Inc.	SEBS	Elastron® G
Lapex R G/10	LATI S.p.A.	PPSU	Lapex