Premi-Glas® 2200-15 CR-SX

Category:	TS, Unspecified , Thermoset, Unspecified
Manufacturer:	Premix, Inc.
Trademark:	Premi-Glas®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Odol1n_Premi-Glas-2200-15-CR-SX.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Premi-Glas® 2200-15 CR-SX is a fiberglass reinforced thermoset sheet molding compound for electrical, flame retardant, and HVAC applications.

Key Features and Benefits:

Pigmentable for molded-in color; best appearance with mold texture.

Good dimensional stability, including excellent thermal resistance.

UL 94-5V flame resistance at 1.5mm minimum thickness.

Subject to UL746C for consideration in exterior applications involving UV exposure and water immersion. File E42524.

General Information
Filler / Reinforcement	Glass fiber reinforced material
Features	Good dimensional stability Good corrosion resistance Flame retardancy
Uses	Electrical/Electronic Applications
UL File Number	E42524

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.70 - 1.85	g/cm³
Molding Shrinkage - Flow	0.15 - 0.35	%
Shrinkage	0.15	%	ISO 2577

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (Compression Molded)	8960	MPa	ASTM D638
Tensile Strength (Compression Molded)	31.0	MPa	ASTM D638
Flexural Modulus (Compression Molded)	8270	MPa	ASTM D790
Flexural Strength (Compression Molded)	100	MPa	ASTM D790
Poisson's Ratio	0.30

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (Compression Molded)	510	J/m	ASTM D256
Unnotched Izod Impact (Compression Molded)	690	J/m	ASTM D4812

Thermal	Nominal Value	Unit	Test Method
Linear thermal expansion coefficient
Flow ¹	2.5E-5	cm/cm/°C
Lateral ²	3.5E-5	cm/cm/°C
Thermal Conductivity	0.30	W/m/K
RTI Elec	130	°C	UL 746
RTI Imp	130	°C	UL 746
RTI	130	°C	UL 746

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength	15	kV/mm	ASTM D149
Arc Resistance	180	sec	ASTM D495
Comparative Tracking Index	600	V	ASTM D2303

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.50 mm)	V-0 5V		UL 94

Injection	Nominal Value	Unit
Mold Temperature	149	°C
Injection Pressure	3.45 - 6.89	MPa

Note Message
1 .	XY Direction
2 .	Z Direction

Resin Grade	Manufacturer	Category	Trademark
Shin-Etsu Elastomer KE-941U	Shin-Etsu Silicones of America	Silicone Rubber, HTV	Shin-Etsu Elastomer
VisiJet® FTI Blue	3D Systems	Unspecified	VisiJet®
DJSilicone NE-G151	DONGJUE SILICONE (NANJING) CO., LTD	Silicone	DJSilicone
HIPOL™ J700	Mitsui Chemicals, Inc.	PP Homopolymer	HIPOL™
Sylvin 6185-80 Blue 8284	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin