HANWHA LLDPE 3303
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Oc8RFa_HANWHA-LLDPE-3303.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HANWHA LLDPE 3303 is manufactured by Spherilene process and designed for general purpose film. LLDPE 3303 has well balanced property of mechanical property and processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.924 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 22.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 900 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm | 40.2 | MPa | ASTM D882 |
| TD : Break, 30 µm | 36.3 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm | 500 | % | ASTM D882 |
| TD : Break, 30 µm | 700 | % | ASTM D882 |
| Dart Drop Impact (30 µm) | 100 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD : 30.0 µm | 117.7 | kN/m | ASTM D1004 |
| TD : 30.0 µm | 122.6 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -76.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 105 | °C | ASTM D1525 |
| Melting Temperature | 125 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm) | 14 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2 to 3Optimum Gage Range: 0.02 to 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 208A | RTP Company | Nylon 6 | RTP |
| Starex VE-0860SE | SAMSUNG SDI CO., LTD. | ABS | Starex |
| Sumikon® PM-9640 (Compression) | Sumitomo Bakelite North America, Inc. | Phenolic | Sumikon® |
| ALCOM® ABS 530/22 SV1287-04MCS | ALBIS PLASTIC GmbH | ABS | ALCOM® ABS |
| Infino VB-3100G | SAMSUNG SDI CO., LTD. | ABS+PBT | Infino |