TAROMID A 260 S
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Obxrrr_TAROMID-A-260-S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 66/6 medium viscosity, high flow, good processing and easy release, low post shrinkage and better dimensional stability, short cycles, high rigidity. Available: natural and colored dry blend (DB). |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 to 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/1.2 kg) | 38 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 1.6 to 2.0 | % | |
| Across Flow | 1.6 to 2.0 | % | |
| Water Absorption | |||
| 23°C, 24 hr | 1.2 | % | ASTM D570, ISO 62 |
| Saturation | 7.4 | % | ASTM D570 |
| Saturation, 23°C | 7.4 | % | ISO 62 |
| Granule Humidity | < 0.15 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 82.0 | MPa | |
| Break | 80.0 | MPa | |
| Tensile Elongation (Break) | 50 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- 1 | 120 | MPa | ISO 178 |
| Break | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 3.8 | kJ/m² | ASTM D256, ISO 179 |
| Charpy Unnotched Impact Strength 3 | |||
| -- | > 300 | kJ/m² | ASTM D256 |
| 23°C | > 300 | kJ/m² | ISO 179 |
| Notched Izod Impact | ISO 180, ASTM D256 | ||
| -20°C, 3.20 mm | 30 | J/m | |
| 23°C, 3.20 mm | 40 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 85.0 | °C | ASTM D648, ISO 75-2/A |
| Continuous Use Temperature | IEC 60216 | ||
| -- 4 | 90.0 | °C | |
| -- 5 | 120 | °C | |
| Vicat Softening Temperature | |||
| -- | 248 | °C | ASTM D1525, ISO 306/A50 6 6 |
| -- | 235 | °C | ASTM D1525, ISO 306/B50 7 7 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 256 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 8.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 9.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | kV/mm | ASTM D149 |
| Comparative Tracking Index | IEC 60112 | ||
| Solution A | > 600 | V | |
| Solution B | 600 | V |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate (2.00 mm) | < 100 | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | V-2 | UL 94 | |
| Glow Wire Ignition Temperature (1.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 24 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 250 to 280 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | Yield |
| 2 . | 6x4x50 mm |
| 3 . | 6x4x50 mm |
| 4 . | 20000 hrs |
| 5 . | Short Term |
| 6 . | Rate A (50°C/h), Loading 1 (10 N) |
| 7 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SRP5602 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| Baydur® 660 IBS (25 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Altuglas® HFI-7 | Altuglas International of Arkema Inc. | Acrylic (PMMA) | Altuglas® |
| LINATHENE® LL120 | USI Corporation | LLDPE | LINATHENE® |
| RTP 128 UV | RTP Company | PP, Unspecified | RTP |