VESTAMID® D DX9325
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | Evonik Industries AG |
| Trademark: | VESTAMID® D |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ObQgZ8_VESTAMID-D-DX9325.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Characterization: 40% glass fiber reinforced, heat-stabilized Applications: plastic-rubber composites Its advantages over PA 12 exhibit in the
The PA 612 compounds of the VESTAMID® D series consequently represent specialty products that complement the comprehensive selection of PA 12 compounds of the VESTAMID® L series. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow | 0.80 | % | |
| Flow | 0.23 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 1.9 | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 9400 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 150 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 4.0 | % | ISO 527-2/1A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C, Complete Break | 16 | kJ/m² | |
| 23°C, Complete Break | 22 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -30°C, Complete Break | 100 | kJ/m² | |
| 23°C, Complete Break | 100 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 210 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 195 | °C | ISO 75-2/A |
| Melting Temperature 2 | 212 | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 55°C) | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | HB | ||
| 3.20 mm | HB |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| ISO Shortname | PA12, MH, 14-100, GF40 | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | specimen 127x12.7x3.2 mm processing acc. to ISO 1874-2 |
| 2 . | 2nd Heating |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Karina WHITE PVC COMPOUND 850-10/99-Y-ERYB | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OXPEKK® IG230C | Oxford Performance Materials, Inc. | PEKK | OXPEKK® |
| Plexiglas® LED white 0V606 | Evonik Industries AG | Acrylic (PMMA) | Plexiglas® |
| EPAMOULD 295A10T | Epaflex Polyurethanes S.R.L. | TPU-Polyester | EPAMOULD |
| MAXAMID™ EPDM036-BK | Pier One Polymers, Inc. | Nylon 6 | MAXAMID™ |