Moplen EP332L
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OZpcS6_Moplen-EP332L.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen EP332L is a heterophasic copolymer and is formulated with a highly effective heat stabilisation package. It exhibits a good fluidity combined with a good balance of impact and stiffness as well as a low warpage tendency. Moplen EP332L is applied in injection moulding applications requiring a good resistance to long term heat exposure, in particular for battery cases and automotive components. Moplen EP332L is suitable for food contact. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.900 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 7.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 9.50 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 53.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1200 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 26.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 8.0 | % | |
| Break | 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.5 | kJ/m² | |
| 0°C | 4.5 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 80 | kJ/m² | |
| 0°C | 140 | kJ/m² | |
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 70.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 148 | °C | ISO 306/A50 |
| -- | 67.0 | °C | ISO 306/B50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 TC-I-20 | RTP Company | PPS | RTP |
| Alpha PVC 2105FR-80 CLEAR 0002 | AlphaGary | PVC, Unspecified | Alpha PVC |
| KOPET® KP133G30 | Kolon Plastics, Inc. | PET | KOPET® |
| INSTRUC PPGB40 | Infinity LTL Engineered Compounds | PP, Unspecified | INSTRUC |
| Karina GRAY PVC COMPOUND 802D18/441-CY-IS-AS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |