Order Products : sales@su-jiao.com

PRIMACOR™ 3003

Category:	EAA , Copolymer
Manufacturer:	The Dow Chemical Company
Trademark:	PRIMACOR™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	OYitIg_PRIMACOR-3003.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PRIMACOR™ 3003 Copolymer is an ethylene acrylic acid copolymer which has been specifically designed by Dow for use as an adhesive or sealant layer in extrusion coating and extrusion lamination.

PRIMACOR 3003 Copolymer exhibits:

Excellent draw-down and edge stability

Excellent organoleptic properties

Excellent toughness and strength

Outstanding environmental stress crack and product resistance

Excellent hot-tack and sealability

Adhesion to paper, paperboard, metals and polyethylenes

Insensitivity to moisture

Applications:

Flexible packaging laminates

Liquid packaging board laminates

Complies with:

U.S. FDA 21 CFR 177.1310(a)(1)

EU, No 10/2011

Consult the regulations for complete details.

General Information
Agency Ratings	EU No 10/2011 FDA 21 CFR 177.1310 (a) 1
Forms	Pellets
Processing Method	Extrusion Coating

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.935	g/cm³	ASTM D792, ISO 1183
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	7.8	g/10 min	ASTM D1238, ISO 1133
Comonomer Content ¹	6.5	%	Internal Method

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus - 2% Secant	130	MPa	ASTM D638, ISO 527-2
Tensile Strength			ASTM D638, ISO 527-2
Yield	7.50	MPa
Break	18.0	MPa
Tensile Elongation (Break)	590	%	ASTM D638, ISO 527-2

Films	Nominal Value	Unit	Test Method
Seal Initiation Temperature ²	90.0	°C	Internal Method

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	90.0	°C	ISO 306/A
Melting Temperature (DSC)	100	°C	Internal Method

Extrusion	Nominal Value	Unit	Test Method
Melt Temperature	260 to 290	°C
Minimum Coating Weight (290°C)	8.0	g/m²	Internal Method
Neck-in ³(290°C)	45.7	mm	Internal Method

Note Message
1 .	Comonomer content measured by a Dow proprietary method that has equivalent accuracy as compared to ASTM D 4094.
2 .	25 g/m² coatings at 290°C set temperature.
3 .	at 100 m/min, 25 g/m² coatings

Resin Grade	Manufacturer	Category	Trademark
TECHNYL® A 218G V33 BLACK 34N	Solvay Engineering Plastics	Nylon 66	TECHNYL® A
Small Boss RPVC001	Tongxiang Small Boss Special Plastic Products Co., Ltd.	PVC, Rigid	Small Boss
Tenopom® POM B3 MF TZ NTLA010 PR318	Petropol Industry and Trade of Polymers LTDA	Acetal (POM) Copolymer	Tenopom® POM
Enerlon Enerlon	Greene, Tweed & Co.	PTFE	Enerlon
LNP™ LUBRICOMP™ FX86496 compound	SABIC Innovative Plastics	PE, Unspecified	LNP™ LUBRICOMP™