REPOL® B250EG
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | REPOL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OWuEpI_REPOL-B250EG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Repol B250EG is recommended for use in Extrusion Coating process where high flow is required. It is an ideal material to use in coating of polypropylene woven fabrics. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, Injection Molded) | 24.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Yield, Injection Molded) | 6.0 | % | ASTM D638 |
| Flexural Modulus - 1% Secant (Injection Molded) | 900 | MPa | ASTM D790A |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, Injection Molded) | 50 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 95.0 | °C | ASTM D648 |
| Note Message | |
|---|---|
| 1 . | Type I, 50 mm/min |
| 2 . | Type I, 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Queo™ 0230 | Borealis AG | Plastomer | Queo™ |
| Tenac™ 4013A | Asahi Kasei Chemicals Corporation | Acetal (POM) Homopolymer | Tenac™ |
| Ultraform® N 2520 L | BASF Corporation | Acetal (POM) Copolymer | Ultraform® |
| KOPA® KN133G50GR | Kolon Plastics, Inc. | Nylon 6 | KOPA® |
| INSULCAST® 987 CM | ITW Polymers Coatings North America | Epoxy | INSULCAST® |