LNP™ LUBRICOMP™ KG002 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | OWbbGH_LNPLUBRICOMPKG002compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP LUBRICOMP KG002 is a compound based on Acetal Copolymer containing Graphite. Added features include : Internally Lubricated. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.46 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 2.0 | % | Internal method |
| Water Absorption (23°C, 24 hr) | 0.31 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/5 | ||
| Yield | 53.0 | MPa | ISO 527-2/5 |
| Fracture | 53.0 | MPa | ISO 527-2/5 |
| Tensile Strain | ISO 527-2/5 | ||
| Yield | 5.1 | % | ISO 527-2/5 |
| Fracture | 5.1 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 3100 | MPa | ISO 178 |
| Flexural Stress | 86.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| With self-dynamics | 0.56 | ASTM D3702 Modified | |
| With Self-Static | 0.44 | ASTM D3702 Modified | |
| Wear Factor - Washer | 103 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 5.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 40 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, unannealed, 64.0mm span | 139 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 97.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 - 188 | °C | |
| Middle Temperature | 193 - 204 | °C | |
| Front Temperature | 210 - 221 | °C | |
| Processing (Melt) Temp | 199 - 216 | °C | |
| Mold Temperature | 82.2 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sindustris PP HR2101D | Sincerity Australia Pty Ltd. | PP, Unspecified | Sindustris PP |
| Starflam P10002Z | Eurostar Engineering Plastics | Nylon 6 | Starflam |
| TRIPET® 2500G30 | Samyang Corporation | PET | TRIPET® |
| LEXAN™ HP2REU resin | SABIC Innovative Plastics Europe | PC | LEXAN™ |
| Rotuba CAP CP808 (12% Plasticizer) | Rotuba Extruders, Inc. | CAP | Rotuba CAP |